CAD/CAM K2 Zirkonblanks translucent Ø 98,5-10mm
Yeti Dentalprodukte · #397-0010
Automatisch erfasst von onlineshop.yeti-dental.com
Sie sind der Hersteller?Daten liefern
Herstellertext auf Englisch
K2 zircon blanks translucentnatural-looking aesthetic resultsreduction of brightness level due to high translucencylow light reflectionnatural adaptation to another teethsuitable for large-span bridges till 14 units but with max. 2 ponticsparticular good biologial compatibilityhomogenous density and very fine grain for smooth milling resultshigh edge stability material properties Density:6.08 g/cm3Flexural strength (biaxial):>1100 MPaGrain size:<0.4 µmBreaking strength:5 MPavmVickers hardness HV10:1250Translucency (1mm, D65):41 %CTE:10 10-6 /KThermal conductivity:2.5 W/mKDissolubility:≤50 µg/cm2Product overview K2 zircon blanks translucentStrengthØ 95,0Ø 98,510,0 mm397-1010397-001012,0 mm397-1012397-001214,0 mm397-1014397-001416,0 mm397-1016397-001618,0 mm397-1018397-001820,0 mm397-1020397-002025,0 mm397-1025397-0025Downloads Instruction manual 3.0 Safety data sheet 1.1 old documents (click here): Instruction manual 1.0 Manual 2.0
Produktinformationen
| Hersteller | Yeti Dentalprodukte |
|---|---|
| Wärmeausdehnungskoeffizient (WAK) | 10 10⁻⁶ /K |
| Typ | K2 translucent |
| Kraft | 10,0 mm |
| Gewicht | 0,31 kg |
| Dichte | 6,08 g/cm³ |
| Material | Zircon |
| Korngröße | <0,4 µm |
Dokumente
- Safety data sheet 1.1Sicherheitsdatenblatt
- Instruction manual 1.0Dokument
Dokumente zur Produktlinie
- Betriebsanleitung 3.0Dokument
- Sicherheitsdatenblatt 4.0Sicherheitsdatenblatt
- Sicherheitsdatenblatt 1.0Sicherheitsdatenblatt
- Sicherheitsdatenblatt 3.0Sicherheitsdatenblatt
- Betriebsanleitung 1.0Dokument
- Betriebsanleitung 2.0Dokument