Fusion AM is a CoCr dental alloy powder with improved properties for the production of dentures in the laser melting process.
The dental alloy is a CoCr composition that is already established on the market and has been redesigned and improved by Scheftner.
Due to its composition, the powder is suitable for SLM systems that are already on the market, without the need for process and parameter changes.
The manufacturing process of the powder ensures the best flowability and consequently the security of a homogeneous coating
Key Features:
- Grain size of the alloy powder: +10/-45µm
- Indications according to DIN EN ISO 22674, Type 5
Composition in percent by mass:
| Element | Percentage |
|---|---|
| Co | 63,9% |
| Cr | 24,7% |
| W | 5,4% |
| Mo | 5,0% |
| Si | 1,0% |
| C,Fe,Mn,N | <1% |
Technical properties:
| Property | Value |
|---|---|
| Proof stress (Rp 0.2) | 1210MPa |
| Ultimate tensile strength | 1440MPa |
| Elongation | 3% |
| Elastic modulus | 230GPa |
| Vickers hardness | 540HV 10 |
| Density | 8,7g/cm³ |
| CTE (25-500°C) | 14,1 x 10⁻⁶K⁻¹ |
| Laser weldable | Ja |
| Type (DIN EN ISO 22674) | 5 |
Note: Standard values; dependent on specific machine settings. Determined after thermal treatment / Simulation of ceramic firing
Trade unit:
5000g
Informations produit
| Fabricant | S&S Scheftner |
|---|---|
| Densité | 8,7 g/cm³ |
| Dureté | 540 HV 10 |
| Elongation | 3% |
| Indications | DIN EN ISO 22674, Type 5 |
| Taille des grains | +10/-45µm |
| Allongement à la rupture | 3% |
| Résistance à la traction | 1440 MPa |
| Elasticity Modulus | 230 GPa |