MoguCast EH
CoCr partial denture alloy for sophisticated combined restorations. Free of nickel, beryllium, lead and cadmium. Type 5 pursuant to DIN EN ISO 22674.
Features:
- Excellent degree of purity
- Biocompatible and extremly corrosion resistant
- High wearing comfort due to low thermal conductivity
- Spring hard
Advantages for dental technicians:
- Particularly suitable for extremely graceful removables
- Ideal alloy for restorations which are exposed to very high loads
- Excellent for casting of 3D printed plastic parts
- Universally applicable for clasp-retained prostheses and combined techniques
- Pleasant polishing properties and easy finishing
- Optimal conditions for laser welding
- System-free working due to very good alloy properties
Composition:
- Co: 62%
- Cr: 25%
- W: 9%
- Nb: 2%
- C, V, Mo, Mn, Si: <1%
Technical properties:
- Proof stress (Rp 0.2): 662 MPa
- Ultimate tensile strength: 877 MPa
- Elongation: >4%
- Elastic modulus: 200 - 210 GPa
- Vickers hardness: 420 HV 10
- Density: 8.7 g/cm³
- Melting range: 1320 - 1400°C
- Preheating temperature: 850 - 950°C
- Casting temperature: 1500 - 1550°C
- Laser weldable: Yes
- Type (DIN EN ISO 22674): 5
Trade unit:
1000g
Informations produit
| Fabricant | S&S Scheftner |
|---|---|
| Densité | 8,7 g/cm³ |
| Dureté | 420 HV 10 |
| Elongation | >4% |
| Température | 1500 - 1550°C |
| Allongement à la rupture | >4% |
| Plage de fusion | 1320 - 1400°C |
| Résistance à la traction | 877 MPa |
| Elasticity Modulus | 200 - 210 GPa |
| Température de préchauffage | 850 - 950°C |