Starbond Easy Disc
S&S Scheftner · #140508
Collecté automatiquement depuis scheftner.dental
Vous êtes le fabricant ?Transmettez vos données
Texte du fabricant en anglais
CoCrW Milling Disc
CoCrW milling disc outstanding for manufacturing of crowns, bridges, frameworks, telescopes, bars, attachments and implant-supported superstructures. Starbond Easy Disc is based on a proven veneering alloy already used in conventional casting technique. Free of nickel, lead, beryllium and cadmium. Type 4 pursuant to DIN EN ISO 22674.
Advantages for users:
- Medium hardness of 289 HV 10
- Excellent metal-ceramic Bonding
- Biocompatible
- Easy polishing
- Laser weldable
- Dry and wet milling
Composition in percent by mass:
- Co: 61%
- Cr: 27.5%
- W: 8.5%
- Si: 1.6%
- C,Mn,Fe: <1%
Technical properties:
- Proof stress (Rp 0.2): 416MPa
- Ultimate tensile strength: 663MPa
- Elongation: 18%
- Elastic modulus: 191GPa
- Vickers hardness: 289HV10
- Density: 8.6g/cm³
- CTE (20-500°C): 14.3 x 10⁻⁶K⁻¹
- CTE (20-600°C): 14.6 x 10⁻⁶K⁻¹
- Laser weldable: Yes
- Type (DIN EN ISO 22674): 4
Informations produit
| Fabricant | S&S Scheftner |
|---|---|
| Densité | 8,6 g/cm³ |
| Caractéristiques | 不含镍、铍、铅和镉；可干铣和湿铣；容易上光 |
| Dureté | 289 HV10 |
| Matériau | CoCrW |
| Elongation | 18% |
| Composition | Co 61%, Cr 27.5%, W 8.5%, Si 1.6%, C,Mn,Fe <1% |
| Applications | 牙冠、长桥、支架、套筒冠义齿、杆式支撑、附着体义齿、种植体支撑的上部结构和基台 |
| Allongement à la rupture | 18% |
| Résistance à la traction | 663 MPa |
| Limite d'élasticité | 416 MPa |
| Résistance à la traction | 663 MPa |
| Elasticity Modulus | 191 GPa |
| Allongement à la rupture | 18% |